PE Geo Membrane Used for Lotus Pond Liners

Nov-15-2017

PE Geo Membrane Used for Lotus Pond Liners Basic Info

Model NO.: pe geo membrane
Application: Waterproof
Waterproof Membrane Yield Elongation(%): 12
Dimensional Stability(%): ±2
Material: HDPE
Waterproof Membrane Density (g/cm3): 0.939
Breaking Elongation(%): 700
Product Name: PE Geo Membrane Used for Lotus Pond Liners
Specification: CE
HS Code: 39219090

PE Geo Membrane Used for Lotus Pond Liners Product Description

PE Geo Membrane Used for Lotus Pond Liners HDPE Smooth GeoMembrane Description:

Smooth HDPE Geomembrane(HTPLASTIC) is a black, high quality, high density polyethylene geomembrane produced from specially formulated, virgin polyethylene resin.

The polyethylene resin is designed specifically for flexible and durable geomembrane applications, it contains approx. 98% polyethylene, 2% carbon black and trace amounts of antioxidants and heat stabilizers, dimensional stability and thermal agin characteristics, HT PLASTIC Geomembrane has excellent resistance to UV radiation and is suitable for exposed applications.

HDPE Smooth GeoMembrane Application:

Geomembrane used in groundsill of road, highway, railway and waterproof layer of swelling clay and wet collapsed loess. Geomembrane can be widely used in areas of garbage burying, waste disposal and underground construction projects. Such as below:

- aquaculture ponds
- Ouchi root barrier membrane
- Floating baffles;
- Process wastewater
- Stormwater impoundments;
- Secondary containment;
- Spill containment
- Manure and biogas tanks and covers
- Potable water tanks and covers;
- Sludge Drying beds;
- Bioremediation covers & liners;
- Leachate ponds

pond liners HDPE Sheet Liner Smooth HDPE Geomembrane
HDPE Geomembrane specifications(CJ/T234-2006)(USA GRI-GM13 Standards)
NO.	Value(mm)	0.75	1.00	1.25	1.50	2.00	2.50	3.00
1	Density (g/cm3)	0.939
2	Tensile propeties
	Yield strength(N/mm)	11	15	18	22	29	37	44
	breaking strength(N/mm)	20	27	33	40	53	67	80
	Yield elongation(%)	12
	breaking elongation(%)	700
3	Tear resistance(N)	93	125	156	187	249	311	374
4	Puncture resistance(N)	240	320	400	480	640	800	960
5	hstress crack resistance	300
6	carbon black
	carbon black content(%)	2.0~3.0
	carbon black dispersion	carbon black dispersion(only near spherical agglomerates)for
		10different views 9 in categorise 1 0r 2 and 1 in category
7	Oxidative induction time(OIT)
	standard OIT (min)	100
	High pressure OIT (min)	400
8	Oven aging at 85oC
	standard OIT-% retained after 90 days(%)	55
	High pressure OIT-% retained alw 90 days(%)	80
9	UV Resistance
	standard OIT retained after 1600hrs(%)	50
	High pressure OIT retained after 1600hrs(%)	50
10	Low temperature impaci brinle at -70oC	pass
11	permeability(g.cm/cm2.s.Pa)	≤1.0×10-13
12	Dimensional stability(%)	±2